HTVF-1300-A-R Atmosphere furnace is a roller table atmosphere furnace with 1300ºC max working temperature and L80xW40xH875cm. The roller furnace is designed for simulating a big continuous kiln to find suitable sintering parameters at a low cost, and it is excellent to make cathode materials for a pilot test of battery research.
HTVF-1300-A-R Atmosphere furnace is a roller table atmosphere furnace with 1300ºC max working temperature and L80xW40xH875 cm. The roller furnace is designed for simulating a big continuous kiln to find suitable sintering parameters at a low cost, and it is excellent to make cathode materials for a pilot test of battery research.
Furnace Features | Two heating zone (top and bottom) with ceramic rollers table in the middle to produce rapid heating Heating elements are made of SiC rods with max. 1400ºC working temperature The heating module is placed inside a vacuum chamber for atmosphere control from oxygen to inert gases. 800 mm L heating zone (112 Liter capacity) Dual programmable temperature controllers provide +/-1ºC accuracy Three flowmeters are installed for gas flow control An oxygen analyzer built in for monitoring oxygen content during processing |
Power | AC 440V (+/-10%), three-phase, 50/60 Hz (380VAC, 3 phases is available upon request) 35KW max 10-foot power cable included but without plug |
Heating chamber | SiC rod as heating elements Heating Zone: L 800 x W 400 x H 350 mm (112 liter capacity) Constant temperature zone: 660 mm with +/- 5ºC Almina ceramic rods are middle of the heating chamber to hold the multi crucibles Max. working temperature: 1300°C max (< 2 hours) and 1200°C (continuous) Max heating rate: 10 ºC/s |
Vacuum chamber | The heating module is placed into a stainless steel vacuum chamber with KF 40 vacuum port Dail vacuum gauge Gas inlet and outlet port (1/4) Two hinged types doors for loading and unloading samples Vacuum level: 10-1 torr for the use of oxygen, and 10-2 torr for the use of inerts gases Positive pressure: < 0.5 bar |
Temperature Control | Two temperature controllers for controlling two zones independently via SCR PID automatic control with up to 30 programmable segments for precise control of heating rate, cooling rate, and dwell time. Over-temperature protection and alarm allow for operation without attendant(s). Two S-type thermal couples are included ± 1 ºC temperature accuracy for dwelling. RS485 Communications Port. |
Crucibles (optional) | Four Alumina Saggar (330x330 x120 mm) can be placed inside the furnace by the double layer Each alumina sagger can handle 20 kg NMC powder and 80 kg powder can be sintered per batch 24 small alumina saggers (140x140x66 mm) can be placed via two rows x 3 layers (4x2x3) Each alumina sagger can handle 2 kg NMC powder, and 48 kg per batch |
Space required | 3 x3 meter |
Net Weight | ~1300 Kg |
Warranty | One-year limited manufacturer's warranty (Consumable parts such as processing tubes, O-rings, and heating elements are not covered by the warranty, please order replacements at related products below). |
HTVF-1300-A-R Atmosphere furnace is a roller table atmosphere furnace with 1300ºC max working temperature and L80xW40xH875 cm. The roller furnace is designed for simulating a big continuous kiln to find suitable sintering parameters at a low cost, and it is excellent to make cathode materials for a pilot test of battery research.
Furnace Features | Two heating zone (top and bottom) with ceramic rollers table in the middle to produce rapid heating Heating elements are made of SiC rods with max. 1400ºC working temperature The heating module is placed inside a vacuum chamber for atmosphere control from oxygen to inert gases. 800 mm L heating zone (112 Liter capacity) Dual programmable temperature controllers provide +/-1ºC accuracy Three flowmeters are installed for gas flow control An oxygen analyzer built in for monitoring oxygen content during processing |
Power | AC 440V (+/-10%), three-phase, 50/60 Hz (380VAC, 3 phases is available upon request) 35KW max 10-foot power cable included but without plug |
Heating chamber | SiC rod as heating elements Heating Zone: L 800 x W 400 x H 350 mm (112 liter capacity) Constant temperature zone: 660 mm with +/- 5ºC Almina ceramic rods are middle of the heating chamber to hold the multi crucibles Max. working temperature: 1300°C max (< 2 hours) and 1200°C (continuous) Max heating rate: 10 ºC/s |
Vacuum chamber | The heating module is placed into a stainless steel vacuum chamber with KF 40 vacuum port Dail vacuum gauge Gas inlet and outlet port (1/4) Two hinged types doors for loading and unloading samples Vacuum level: 10-1 torr for the use of oxygen, and 10-2 torr for the use of inerts gases Positive pressure: < 0.5 bar |
Temperature Control | Two temperature controllers for controlling two zones independently via SCR PID automatic control with up to 30 programmable segments for precise control of heating rate, cooling rate, and dwell time. Over-temperature protection and alarm allow for operation without attendant(s). Two S-type thermal couples are included ± 1 ºC temperature accuracy for dwelling. RS485 Communications Port. |
Crucibles (optional) | Four Alumina Saggar (330x330 x120 mm) can be placed inside the furnace by the double layer Each alumina sagger can handle 20 kg NMC powder and 80 kg powder can be sintered per batch 24 small alumina saggers (140x140x66 mm) can be placed via two rows x 3 layers (4x2x3) Each alumina sagger can handle 2 kg NMC powder, and 48 kg per batch |
Space required | 3 x3 meter |
Net Weight | ~1300 Kg |
Warranty | One-year limited manufacturer's warranty (Consumable parts such as processing tubes, O-rings, and heating elements are not covered by the warranty, please order replacements at related products below). |